TITANIT ANTI CORROSION PRIMERS
Get Price Quote
We offer Titanit Anti Corrosion Primers made from superior and high quality materials. Due to their excellent adhesion properties to zinc, steel and aluminum surfaces, TACP act as a reliable and strong corrosion protection mechanism. TACP are designed for priming of metal and wooden surfaces for coating with various enamels. With a shelf life of 24 months, the primer can be stored at a temperature of up to 35 degree centigrade.Anticorrosion primers which acts as “ Anti Corrosion Coating for Flame retardant systems / Steel Reinforcement Coating (Titanit)Anticorrosion coating for flame retardant systems Steel reinforcement coating Titanit- Primeranticorrosion Primers - (1 Component)Base: one - component ,% : 55 ± 2% by volume; 2 + 68% by weight Solids Volume,% : 55 ± 2% by volume; 2 + 68% by weightDensity: 1.3-1.4 kg / liter (ready to apply mixture)Drying time: at a temperature of 20 ± 2 ° C is 24 hoursFilm thickness: 0,50-1,0 mm Consumption: 0,10-0,13 kg / m2The fineness degree: 50 micronsWarranty period of storage :12 months from date of manufacture. The main advantages Sphere of application Material properties, specificationsApplication: Excellent adhesion to steel, zinc and aluminum surfaces; Short recoating time; Reliable corrosion protection Easy application"Titanit" primer is designed for priming of metal (ferrous metals) and wooden
surfaces for coating with various enamels. "Titanit " primer is universal, used in complex covering with almost all fillers and finishingenamels, and can also be used as an independent coating. Primer is very comfortable in use,applied by various methods. "Titanit" primer meets the state sanitary epidemiological rules and standards.High resistance to climatic influences in rural, urban and industrial atmosphere, to mineral oils and greases.Can be used as a standalone coating under the same conditions.The film has a high resistance to common purpose nitro enamels.Resistant to temperatures from -45 to +60 ° C. primerPneumatic and airless spraying, spraying in electric fields, jet flow coating, dipping, brush in two layers Apply at ambient temperature of +5 to +35 ° C and relative humidity of 80%. Temperature of the substrate must be at least 3 ° C above the dew point. "Titanit" primer is compatible to the most of decorative and finishing paints and varnishes.Consumption Thickness Storagesingle layer of primer is 100-130 g / m². single layer is 20-25 microns, two layers - 40-50 microns.Drying time of each layer at a temperature of 20 ± 2 ° C - 24 hours. It is permitted to dry the primer at 105 ± 5 ° C during 35 min. After drying, before applying the enamel, the primer coating is incubated during 3 h at a temperature of 20 ± 2 ° C. The primer is stored at a temperature of -40 to + 40 ° C.Feature on the basis: two - component (base + hardener)Solids Volume,% - 50 + 2% by volume (68 + 2% by weight)The ratio of mixing the base and hardener - 4: 1 (by volume)Pot life of mixture - up to 6 hours at +23 ° CFilm thickness - 0,50-1,0 mmConsumption - 0,12 - 0,25 kg/m²Packaging - Base 16 L / hardener 4LShelf-life : 24 months The temperature at transportation and storage: 0° C - +35 ° CTechnology of formation of primer-layer: Technology of the primer-layer formation must meet the requirements of technological regulations (instructions) to the applicable fire protection means, as well as the requirements and instructions for the formation andoperation of coating based on primer "Titanite-EP Primer» â�� 004-I / Y.Basic conditions while performing works on application of the primer on treated metal Dry, clean, degreased surface, free of corrosion, scale, etc. Ambient Temperature - min +5 ° C. The relative humidity - less than 85%. Temperature of the painted steel structure surface must be above the dew point of not less than 3 ° C.Technical description: "titanit- Ep Primer" is used for forming the primer layer in the systems of flame retardants based on fire retardant pain "titanit- Ep Primer, "GARANT-M" for steel structures, as well as the "TITAN-ST", "TITAN 225-B " for concreteStructures : In addition, the ground "TITANIT- EP PRIMER"is used for priming of steel, aluminum, zinc and concreteSurfaces : exposed to mechanical and / or chemical attack, both inside and outside the premises."TITANIT- EP PRIMER" is recommended as a corrosion protection of building frameworks, tubular bridges, bases forpriming concrete structures transport tunnels.Documentation:Certificate of compliance: Technological instruction number 004-I / Y on the formation andoperation based on coating primer "TITANIT- EP PRIMER".
...more
+3
+4
Post Free Ad